Clothing signs silicon rubber CY-1300F
Overview
This product is a two -component plus -shaped liquid silicon rubber. It has excellent weather resistance, good size stability, high transparency, non -toxic and environmental protection, prominent adhesion with various fabrics, outstanding three -dimensional effect effects, can be at high temperature at high temperature, can be at high temperatures. Quickly solidify. This product is widely used in various types of socks, gloves and other clothing and strap products. The non -slip and elastic and stretching reinforcement of webbing products.
Index
Appearance (component A/ B) colorless transparent liquid/ transparent viscous liquid
Viscosity (component B) (MPA · S) 90000-110000
Operation time (30 ºC) (h) ≥48
Hardness (Shore a) 35-40
Stretch strength (MPA) ≥4.0
Elongation (%) ≥350
Tear intensity (kn/m) ≥10.0
Density (G/CM3) 1.10-1.12
Performance
Double component, 2: 100
Excellent weather resistance
Good size stability
Non -toxic and environmental protection
The adhesion of higher transparency
Application field
The non -slip and elastic and stretching reinforcement of all kinds of socks, gloves and other clothing and strap products can be used
Instructions
1. Plates: Planning is mixed at a weight ratio of 2: 100 (the amount of the increase in the increase of the A component will accelerate the curing speed), and the mixing can be mixed artificially or using the device mixed.
2. Taste: The mixed glue should be vacuum -off before making a sign or printing a trademark on the fabric. Under vacuum, the volume of the rubber can increase by 2-4 times. Therefore, the off-bubble container should be 2-4 times larger than the volume of the glue. Ten minutes) is the end of the off -bubbles, and it can be performed in a vacuum dryer when used in small amounts. If it is used for the screen printing process, it can be used without driving.
3. For molding: The glue after decoction can be heated for molding. The glue not to bubble can be scraped in the screen printing frame.
4. Avoid contact with contracted silicone rubber curing agent during operation. Allows that may cause non -solidification are amine, sulfur, phosphorus compounds and some metal salts. During use, the tide should be avoided.
5. It is recommended to put the rubber in a container and stir, and then add the curing agent to stir well.
Application field
The non -slip and elastic and stretching reinforcement of all kinds of socks, gloves and other clothing and strap products can be used
Packing and storage
Packaging: CY-1300F A components: 2kg/pot, 20kg/barrel
CY-1300F B: 20kg/barrel, 200kg/barrel lining plastic bag storage: there is dry, ventilated and cool place
Human shelf life: 12 months, it can restore its liquidity under the action of shear force (strong stirring).